COMPUTER MODELLING OF LOW-MELTING-POINT MATERIALS SEMICONTINUOUS DIRECT EXTRUSION TEMPERATURE CONDITIONS
DOI:
https://doi.org/10.14529/met200404Keywords:
direct wire extrusion, semicontinuous extrusion, computer modeling, deformation heating, extrusion temperatureAbstract
The heating of metal and tooling caused by deformation processes and contact friction is the reason for a decrease in the finished product quality and a loss of process stability during cold direct extrusion of low-melting-point materials. PJSC Chelyabinsk Zinc Plant together with the Department of Metal Forming Processes and Machines of SUSU has been actively and successfully developing and mastering the technology for the production of wire and rod solder from POIn-52 alloy. A computer simulation of the extrusion process temperature conditions of the POIn-52 alloy wire with a diameter of 2.0 mm at an extrusion speed of 0.5; 1.0 and 3.0 mm/s from a workpiece with a diameter of 20 mm was carried out in this work, using a specialized engineering package QForm. Based on the results of computer simulation, it has been established that the speed of metal outflow from the die, which in turn is determined by the extrusion speed and the extrusion ratio, has a significant effect on the pressing process temperature conditions. The metal temperature increases from 33.4 to 75.8 °C, when the extrusion speed changes from 0.5 to 3 mm/s in the extrusion process of wire 2.0 mm from a billet 20 mm. Moreover, it should be noted that sequential extrusion of four blanks leads to an increase in the wire temperature from 75.8 to 87 °C. This is due to the fact that in the process of continuous extrusion the tooling, namely the drawing die, heats up and after the fourth extrusion cycles its average temperature is about 45 °C. The average container temperature rises by 4 °C. A further increase in the temperature of both the metal being extruded and the wire on the investigated diameter of the solder stops and the process stabilizes after the fourth cycle.References
Shakhnova V.A. (Ed.) Konstruktorsko-tekhnologicheskoye proyektirovaniye elektronnoy apparatury: ucheb. dlya vuzov [Design and technological design of electronic equipment]. Moscow, Publishing house of Bauman MSTU, 2005. 568 p.
Gusev V.G., Gusev Yu.M. Elektronika i mikroprotsessornaya tekhnika: ucheb. dlya studentov vuzov [Electronics and microprocessor technology. A textbook for university students]. Moscow, Higher school Publ., 2006. 799 p.
Medvedev A.M. [Lead-free assembly soldering technologies. What awaits us?]. Electronic components, 2004, no. 11. (in Russ.)
Medvedev A.M. [Electronic components and mounting platforms]. Components and Technologies, 2006, no. 12. (in Russ.)
Grigoriev V. [Lead-free technologies – a requirement of the time or a whim of legislators from the environment?]. Electronic Components, 2001, no. 6. (in Russ.)
Zenin V.V., Belyaev V.N., Segal E.Yu., Kolbenkov A.A. [Lead-free solders in the production technology of microelectronic products]. Microelectronics, 2003, vol. 32, no. 4. (in Russ.)
Bleifrei loten: Silber und Kupfer statt Blei. Krempelsauer. Elektor (BRD), 2000, no. 5.
Shapiro L. [The use of lead-free technologies cannot be avoided]. Bulletin of Electronics, 2007, no. 2. (in Russ.)
Shapiro L. [Implementation of the European RoHS Directive]. Electronic Components, 2006, no. 1. (in Russ.)
Glebov L.A., Radionova L.V., Faizov S.S [Solder POIN-52: process research and development of technology for small-scale wire production]. Magnitogorsk Rolling Practice 2019: materials of the IV youth scientific-practical conference. Ed. A.G. Korchunov. Magnitogorsk, Publishing house of Nosov MSTU, 2019, pp. 54–56. (in Russ.)
Radionova L.V., Faizov S.R., Lezin V.D., Sarafanov A.E. Mathematical Modeling of Direct Extrusion Power Parameters of Low-Melting Materials. Bulletin of the South Ural State University. Ser. Metallurgy, 2020, vol. 20, no. 2, pp. 71–79. (in Russ.) DOI: 10.145–29/met200207
Al-Khuzaie A.S.O., Shirokov V.V., Vydrin A.V. Determination of the Range of Variation of the Parameters of the Stress-Strain State of the Metal during Continuous Pipe Rolling. Bulletin of the South Ural State University. Ser. Metallurgy, 2019, vol. 19, no. 1, pp. 74–79. (in Russ.) DOI: 10.14529/met190109
Torgonin K.S., Shirokov V.V., Chaplygin B.A., Chernobrovin V.P., Plastinin B.G., Kozlov A.V., Dukmasov V.G. Modeling of Pressure Shaping during Manufacturing of Stamp-Welded Pipe Joints. Bulletin of the South Ural State University. Ser. Metallurgy, 2018, vol. 18, no. 4, pp. 109–120. (in Russ.) DOI: 10.14529/met180412
Kharitonov V.A., Yamteeva E.R. [Calculation of preformation parameters based on modeling in the DEFORM 3D software package]. Izvestiya vuzov. Chernaya metallurgiya, 2013, no. 56 (10), pp. 47–48. (in Russ.) DOI: 10.17073/0368-0797-2013-10-47-48
Strugov S.S., Ivanov V.A., Sherkunov V.G. Comparison of Methods of Stress-Strain State Estimation in the Upset of a Cylindrical Workpiece. Bulletin of the South Ural State University. Ser. Metallurgy, 2016, vol. 16, no. 4, pp. 140–146. (in Russ.) DOI: 10.14529/met160416
Lyakishev N.P. (Ed.) Diagrammy sostoyaniya dvoynykh metallicheskikh sistem: sprav. [Diagrams of state of double metal systems]. Vol. 3, book. 1. Moscow. Mechanical Engineering Publ., 2001. 872 p.