Effect of High-Temperature Thermomechanical Treatment on the Properties of a High-Chromium Steel
Keywords:
high-chromium steel, high-temperature thermomechanical treatment, impact toughness, temper brittlenessAbstract
The structure and properties of 20Kh13 (0.2 C–13 Cr) steel are studied after hightemperature thermomechanical treatment (HTTMT) carried out by rolling at 950–900 °C at low strain rate (1 s–1) and up to 30 % true strain. It is found that HTTMT greatly improves impact toughness of the steel after high-temperature tempering. In addition, this treatment effectively retards temper embrittlement by preventing intergranular brittle fracture
References
Бернштейн М.Л. Термомеханическая обработка стали / М.Л. Бернштейн, В.А. Займовский, Л.М. Капуткина. – М.: Металлургия, 1983. – 480 с.
Смирнов, Л.В. Влияние пластической деформации в аустенитном состоянии на хрупкость при отпуске конструкционных легированных сталей / Л.В. Смирнов, Е.Н. Соколков, В.Д. Садовский // ДАН СССР. – 1955. – Т. 103, № 4. – С. 609–610.
Смирнов, М.А. Высокотемпературная термомеханическая обработка и хрупкость сталей и сплавов / М.А. Смирнов, С.Н. Петрова, Л.В. Смирнов. – М.: Наука, 1991. – 167 с.
Диаграммы горячей деформации, структура и свойства сталей: справ. / под ред. М.Л. Бернштейна. – М.: Металлургия, 1989. – 544 с.