QUENCHING AND PARTITIONING (Q&P) PROCESSING OF MARTENSITIC STAINLESS STEELS AISI 414
DOI:
https://doi.org/10.14529/met180410Keywords:
martensitic stainless steels, Q&P heat treatment, stabilization of retained austenite, TRIP effectAbstract
Heat treatment consisting quenching of steel to a temperature inside the martensitic transformation interval with subsequent carbon partitioning between quenched martensite and retained austenite (Q&P treatment) is applied to martensitic stainless steel AISI 414 (Fe – 0.14 % C – 12.5 % Cr – 2.3 % Ni). Q&P processing was modeled using the thermomechanical simulator Gleeble 3800. Phase transformations during processing were studied using a contact dilatometer, which measures the change in the specimen diameter at the thermocouple spot.
After austenitization at 1150 °C for three minutes, the temperature of the onset of the martensitic transformation of the steel under study was 270 °C. To implement Q&P processing, the samples were quenched to temperatures of 250 °C, 200 °C, 150 °C and 100 °C. The carbon partitioning between the quenched martensite and untransformed austenite was carried out in the process of 3-minute exposure at 450 °C.
It has been shown that quenching to temperatures of 200–250 °C with subsequent annealing at 450 °C does not ensure the enrichment of unconverted austenite with carbon, sufficient to suppress martensitic transformation upon subsequent cooling to room temperature. Lowering the quenching temperature to 150 °C with subsequent annealing at 450 °C leads to complete thermal stabilization of the untransformed austenite up to temperatures of minus 60 °C, which ensures a high lowtemperature toughness of the steel under investigation through the TRIP effect, exceeding the values laid down in the requirements for high-strength pipe steel. The conclusion is made about the prospect of Q&P processing of the investigated steel for obtaining a high-strength state with a high level of low-temperature viscosity.
References
Speer J.G., Matlock D.K., De Cooman B.C., Schroth J.G. Carbon Partitioning into Austenite after Martensite Transformation. Acta Materialia, 2003, vol. 51, pp. 2611–2622. DOI: 10.1016/S1359-6454(03)00059-4
Speer J.G., Edmonds D.V., Rizzo F.C., Matlock D.K. Partitioning of Carbon from Supersaturated Plates of Ferrite, with Application to Steel Processing and Fundamentals of the Bainite Transformation. Current Opinion in Solid State Materials Science, 2004, vol. 8, pp. 219–237. DOI: 10.1016/j.cossms.2004.09.003
Edmonds D.V., He K., Rizzo F.C., De Cooman B.C., Matlock D.K., Speer J.G. Quenching and Partitioning Martensite – A Novel Steel Heat Treatment. Materials Science and Engineering, A, 2006, vols. 438–440, pp. 25–34. DOI: 10.1016/j.msea.2006.02.133
Clarke A.J., Speer J.G., Matlock D.K., Rizzo F.C., Edmonds D.V., Santofimia V.J. Influence of Carbon Partitioning Kinetics on Final Austenite Fraction during Quenching and Partitioning. Scripta Materialia, 2009, vol. 61, pp. 149–152. DOI: 10.1016/j.scriptamat.2009.03.02
Speer J.G., De Moor E., Clarke A.J. Critical Assessment 7: Quenching and Partition. Materials Science and Technology, 2015, vol. 31, no. 1, pp. 3–9. DOI: 10.1179/1743284714Y.0000000628
Wang L., Speer J.D. Quenching and Partitioning Steel Heat Treatment. Metallography, Microstructure, and Analysis, 2013, vol. 2, no. 4, pp. 268–281. DOI: 10.1007/s13632-013-0082-8
Somani M.C., Porten D.A., Karjalainen L.P., Misra D.K. Evalution of DQ&P Processing Rout for the Development of Ultra-High Strength Tough Ductile Steels. International Journal of Metallurgical Engineering, 2013, vol. 2 (2), pp. 154–160. DOI: 10.5923/j.ijmee.20130202.07
Jin X. Quenching and Partitioning Heat Treatment: High-Strength Low-Alloys. Encyclopedia of Iron, Steel, and Their Alloys, 2015, pp. 2761–2775. DOI: 10.1081/E-EISA-120051355
Hong S.C., Ahn J.C., Nam S.Y., Kim S.J., Yang H.C., Speer J.D, Matlock D.K. Mechanical Properties of High-Si Plate Steel Produced by the Quenching and Partitioning Process. Metals and Materials Internatinal, 2007, vol. 13, no. 6, pp. 439–445. DOI.org/10.3365/MMI.2007.12.439
Tsuchiyama T., Tobata J., Tao T., Nakada N., Takaki S. Quenching and Partitioning Treatment of a Low-Carbon Martensitic Stainless Steel. Materials Science and Engineering, A, 2012, vol. 532, pp. 585–592. DOI: 10.1016/j.msea.2011.10.125
Tobata J., Ngo-Huynh K.-L., Nakada N., Tsuchiyama T., Takaki S. Role of Silicon in Quenching and Partitioning Treatment of Low-Carbon Martensitic Stainless Steel. ISIJ International, 2012, vol. 52, no. 7, pp. 1377–1382. DOI: 10.2355 /isijinternational.52.1377
Mola J., De Cooman B.C. Quenching and Partitioning (Q&P) Processing of Martensitic Stainless Steels. Metallurgical and Materials Transactions A, 2013, vol. 44A, pp. 946–967. DOI: 10.1007/s11661-012-1420-1.
Bojack A., Zhao L., Morris P.F., Sietsma J. Austenite Formation from Martensite in a 13Cr6Ni2Mo Supermartensitic Stainless Steel. Metallurgical and Materials Transactions A, 2016, vol. 47, no. 5, pp. 1996–2009. DOI: 10.1007/s11661-016-3404-z
Koistinen D., Marburger R. A General Equation Prescribing the Extent of the Austenite-Martensite Transformation in Pure Iron-Carbon Alloys and Plain Carbon Steels. Acta Metallurgica, 1959, vol. 7, pp. 59–60. DOI.org/10.1016/0001-6160(59)90170-1