Appearance of cracks in casing of hot blast duct: numerical estimation of causes
Keywords:
thermal stresses, thermal fatique, cracksAbstract
The heater of blast furnace intended to provide hot blast and has a metal casing lined inside with refractory bricks. The technological process involves cyclic temperature changes of gas in the heater from 400 to 1200°C with cycle duration of 3 hour. After some operating time, cracks appear in the casing. Internal pressure in the apparatus is low, but nevertheless the cracks are dangerous because the stream of hot (1200°C) oxygen-enriched air can damage surrounding structures. A way to prevent cracks depends on the mechanism of their formation. Three possible reasons of the crack formation were considered: uncompensated forces caused by thermal expansion of the entire structure, vibration and thermal stresses due local uneven heating of the casing. Observable cracks have different orientations and in some cases are located sufficiently close to each other. This pattern is characteristic for thermal cracks and is not typical for cracks caused
by mechanical loads and/or vibrations. Numerical analysis shows that the non-uniformity of temperatures may cause the thermal fatigue cracks despite the fact that the non-uniformity observed on the outer surface of the casing is small enough. Fractography had confirmed the thermo-fatigue nature of the cracks. As a possible measure to prevent cracking the usage of 2-layer casing was analyzed; numerical estimations proved potential effectiveness of such solutions.
References
Kalugin Ja.P. [Evolution of Blast Stoves]. Chernaya metallurgiya, 2013, no. 3 (1359), pp. 57–72. (in Russ.)
Kalugin Ya.P. High-Temperature Stoves for Blast Furnaces: New Solutions. Metallurg, 1997, no. 12, pp. 29–30.
Kalugin Ya.P., Prokof'ev B.N., Rudnik V.M. Development of High-Temperature Stoves with a Long Service Life. Steel in Translation, 2000, vol. 30, no. 3, pp. 9–13.
Gokhfel'd D.A., Getsov L.B., Kononov K.M. at al. Mekhanicheskie svoystva staley i splavov pri nestatsionarnom nagruzhenii: sprav. [Mechanical Properties of Steels and Alloys under Nonstationary Loading. Handbook]. Ekaterinburg, Ural Branch of the Russian Academy of Sciences, 1996, 408 p.
Kuskov KV, Kovensky I.M. [Low-Cycle Fatigue of Welded Soy-Indium Steel 09G2S]. Bulletin of the Magnitogorsk State Technical University, 2012, no. 3, pp. 41–44. (in Russ.)
Makhutov N.A., Zatsarinnyy B.B., Bazaras Zh.L. et al. Statisticheskie zakonomernosti malo¬tsiklovogo razrusheniya Statistical regularities of low-cycle fracture [Statistical Regularities of Low-Cycle Fracture]. Moscow, Akademiya nauk SSSR Institut mashinovedeniya im. A.A. Blagonravova, 1989. 252 p.
Normy rascheta na prochnost' oborudovaniya i truboprovodov atomnykh energeticheskikh ustanovok PNAE G-7-002-86 [Strength Codes for the Equipment and Pipelines of Nuclear Power Plants PNAE G-7-002-86]. Moscow, Energoatomisdat, 1989. 525 p.
Gatewood B.E. Temperaturnye napryazheniya primenitel'no k samoletam, snaryadam i yadernym reaktoram [Thermal Stresses with Application to Airplanes, Missiles, Turbines and Nuclear Reactors]. Moscow, Izdatel'stvo inostr. lit., 1959. 359 p.]
Kovalenko A.D. Osnovy termouprugosti [Basics of Thermoelasticity]. Kiev, Naukova Dumka, 1970. 308 p.